 聚对苯二甲酸丁二醇酯，英文名polybutylece terephthalate（简称pbt）

并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。属于聚酯系列，是由1.4-丁二醇(1.4-butylene glycol)与对苯二甲酸(pta)或者对苯二甲酸酯(dmt)聚缩合而成，

此材料的缺点：不耐高温，遇高温易变形

1; 价格相对电木材质便宜
  2; 流注性能好，易成型。此材料的优点：1 韧性佳，不易破碎。

polybutylene terephthalate, english name polybutylene terephthalate (pbt), belongs to the polyester series, is composed of 1.4-pbt butanediol (1.4-butylene glycol) and terephthalic acid (pta) or terephthalate (dmt) and poly condensation, and the mixing procedure made of milky white, translucent to opaque crystalline thermoplastic polyester resin through. collectively, together with the pet thermoplastic polyester, or saturated polyester

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；
3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性。
用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；
2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；
3、工业零件：oa风扇、键盘、钓具卷线器、零件、灯罩等。
特点：pbt为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。pbt
结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。[5]
 
pbt（增强、改性pbt）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显象管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套

pbt is the toughest one of thermal plastic material, it is semi-crystalline materials, chemical stability, mechanical strength, electrical insulating properties and excellent thermal stability. these materials have good stability in a broad range of environmental conditions. pbt hygroscopic properties of very weak. non enhanced tensile strength of pbt is 50mpa, pbt tension strength of glass additive type is 170mpa. glass additives will lead to excessive material embrittlement. pbt; crystallization is rapid, this will cause warpage due to uneven cooling. for glass additive type of material, flow direction shrinkage can be reduced, but with the flow perpendicular to the direction of the shrinkage rate basically no difference and common materials. general shrinkage rate was 1.5%~2.8%. between material shrinkage of 0.3%~1.6% contains 30% glass additive. the melting point (225 ℃) and high temperature deformation temperature is lower than the pet material. veka softening temperature of about 170 ℃. glass transition temperature (glass trasitio temperature) at 22 ℃ to 43 ℃. the crystallization rate of pbt is very high, so its viscosity is very low, cycle time and plastic parts processing are typically low

self lubrication, low friction coefficient, but the volume resistivity, dielectric loss. drawback is the low impact strength, high mold shrinkage. it is mostly filled with glass fiber reinforced or inorganic modification, the tensile strength, bending strength can be increased one times above, thermal deformation temperature is also significantly improved. can work at 140 ℃ long-term, glass fiber reinforced products longitudinal, transverse shrinkage is not consistent, easy to make the products of warping

①注射温度 pbt的分解温度为280℃，所以实际生产中一般控制在240-260℃之间。
②注射压力注射压力一般为50～100mpa。
③注射速率 pbt冷却速度快，因此要采用较快的注射速率。
④螺杆转速和背压
成型pbt的螺杆转速不宜超过80r/min，一般在25～60r/min之间。背压一般为注射压力的10%～15%。
⑤模具温度 一般控制在70～80℃，各部位的温度差不超过10℃。
⑥成型周期 一般情况下为15～60 s。6 注意事项
①再生料的使用 再生料与新料的比例一般在25%～75%。
②脱模剂的使用 一般情况下不使用脱模剂，必要时可采用有机硅脱模剂。
③停机处理
pbt的停机时间在30min以内，可将温度降到200℃时停机。长期停机后再生产时，要将料筒内的料排空，再加入新料才能进行正常生产。
④制品的后处理 一般情况下不需要进行处理，必要时在120℃时处理1～2h。化学和物理特性
pbt是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。pbt吸湿特性很弱。非增强型pbt的张力强度为50mpa，玻璃添加剂型的pbt张力强度为170mpa。玻璃添加剂过多将导致材料变脆。pbt的；结晶很迅速，这将导致因冷却不均匀而造成弯曲变形。对于有玻璃添加剂类型的材料，流程方向的收缩率可以减小，但与流程垂直方向的收缩率基本上和普通材料没有区别。一般材料收缩率在1.5%~2.8%之间。含30%玻璃添加剂的材料收缩0.3%~1.6%之间。熔点（225℃）和高温变形温度都比pet材料要低。维卡软化温度大约为170℃。玻璃化转换温度（glass trasitio
temperature）在22℃到43℃之间。由于pbt的结晶速度很高，因此它的粘性很低，塑件加工的周期时间一般也较低。

1 生产pbt所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

2 优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。                          

3 易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

4 耐热老化性优异，增强后的ul温度指数达到120~140℃，此外，户外长期老化性也很好。

5 耐溶剂好，无应力开裂。

6 优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

7 pbt遇水易分解，在高温、高湿环境下使用需谨慎。

8 pbt易于阻燃，可达ul94v-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

用途：

1、汽车：分电盘盖、车门把手、保险杆、导线护壳、挡泥板、轮圈盖等；

2、工业零件：钓具卷线器、oa风扇.零件、键盘、灯罩等。

3、电子电器：、家电把手.驰返变压器.无熔线断电器、电磁开关、连接器、外壳等；

pbt中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、尺寸安定性良好；2、摩擦系数小有自润性；

3、吸水率低；4、耐药品性、耐油性；5、电气性质优良6、机械性质安定抗张强度与抗张模数和尼龙相似；